3Cr18Mn12Si2N軋制鋼棒 3Cr18Mn12Si2N鍛制鋼棒
3Cr18Mn12Si2N φ10MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ12MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ16MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ20MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ25MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ30MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ35MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ40MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ45MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ50MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ55MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ60MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ65MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ70MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ75MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ80MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ85MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ90MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ95MM(軋材)耐熱鋼棒
3Cr18Mn12Si2N φ100MM(鍛材)耐熱鋼棒
3Cr18Mn12Si2N φ110MM(鍛材)耐熱鋼棒
3Cr18Mn12Si2N φ120MM(鍛材)耐熱鋼棒
3Cr18Mn12Si2N φ130MM(鍛材)耐熱鋼棒
3Cr18Mn12Si2N φ140MM(鍛材)耐熱鋼棒
3Cr18Mn12Si2N φ150MM(鍛材)耐熱鋼棒
3Cr18Mn12Si2N φ160MM(鍛材)耐熱鋼棒
3Cr18Mn12Si2N φ170MM(鍛材)耐熱鋼棒
3Cr18Mn12Si2N φ180MM(鍛材)耐熱鋼棒
3Cr18Mn12Si2N φ190MM(鍛材)耐熱鋼棒
3Cr18Mn12Si2N φ200MM(鍛材)耐熱鋼棒
牌號:3Cr18Mn12Si2N
材料類別:奧氏體耐熱鋼
執(zhí)行標(biāo)準(zhǔn):GB/T1221-1992
特性及適用范圍
3Cr18Mn12Si2N爐用耐熱鋼為奧氏體型鋼,有較高的高溫強度和一定的抗氧化性,并且有較好的抗硫及抗?jié)B碳性。3Cr18Mn12Si2N耐熱鋼有時效脆性,但時效后高溫下仍有較高韌性,可進行剪切、冷熱沖壓和焊接,最高使用溫度約1000℃。3Cr18Mn12Si2N耐熱鋼用于鍋爐吊掛支架、滲碳爐構(gòu)件、加熱爐傳送帶、料盤、爐爪等。
化學(xué)成份:
碳 C :0.22~0.30;
硅 Si:1.40~2.20;
錳 Mn:10.50~12.50;
硫 S :≤0.030;
磷 P :≤0.060;
鉻 Cr:17.00~19.00;
氮 N :0.22~0.33。
力學(xué)性能:
抗拉強度 σb (MPa):≥685;
條件屈服強度 σ0.2 (MPa):≥390;
伸長率 δ5 (%):≥35;
斷面收縮率 ψ (%):≥45;
硬度 :≤248HB。
熱處理規(guī)范及金相組織:
熱處理規(guī)范:固溶1100~1150℃快冷。
金相組織:組織特征為奧氏體型。
一般以熱處理規(guī)范狀態(tài)交貨,其熱處理種類在合同中注明;未注明者,按不熱處理狀態(tài)交貨。
3Cr18Mn12Si2N奧氏體耐熱鋼
上海高高商貿(mào)有限
公司《高高興晟特鋼集團》真實信息、真格品質(zhì)、真實價格提供3Cr18Mn12Si2N奧氏體耐熱鋼。